LSR Free Sample Platinum Silicone Liquid RTV-2 Silicone for Human Part Dolls Sex Toys

• Raw Material: Synthetic Rubber
• Material: Silicone Rubber
• Appearance: Liquid
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Form: Liquid Rubber
• Trademark: Gangtian
• Origin: China
• HS Code: 391000
• Production Capacity: 600 Tons/Month
• Package Size: 11.00cm * 11.00cm * 14.70cm
• Package Gross Weight: 1.000kg

Product Description

Product details:
 

GTSIL-Platinum Series
Platinum cure silicone rubber,which is also named addition cure silicone rubber,is generally a type of two-part liquid silicone rubber vulcanized under room temperature.
Platinum cure silicone rubber is non-hazardus,food-grade,and mainly used for mold making of foods(Candy,cake,chocolate,ice-cake,ect),jewelries,tires,rapid prototyping and vacuum foaming.Besides,it's most suitable for life-casting,such as human parts,sex-toys,silicone dolls,breast paddings,and so on.With a very tiny shrinkage,it's also popular for duplication of concrete blocks.
With appropriate hardness,good tensile&tear strength,and excellent resistance to deformation,finished platinum silicone molds have not only a durable life but also a good performance.

APPLICATIONS:
Technical Data:
Note:
1. The data are based on the operation under room temperature of 25 ºC.
2. Pot life and curing time can be adjusted, and changed by different ratio of catalyst. We recommend 2% to 3% catalyst.
3. Different Colors of base silicone are available , such as red ,pink ,green ,blue ,yellow and so on.
Shelf life:
Eighteen (18) months from date of shipment when stored at 25ºC in the original sealed packages.
How to use:
 

1.Substrate Preparation

The surface of the original should be clean and free of loose material. If necessary, and in particular with porous substrates, use a suitable release agent such as petroleum jelly or soap solution.

2. Mixing
Thoroughly stir Part A (silicone base) before use as filler separation may occur upon prolonged storage.
Weigh 100 grams Part A (silicone base) and 3 grams Part B (curing agent)  in a clean container. Mix together until the curing agent is completely dispersed in the base. Hand or mechanical mixing can be used, but do not mix for an extended period of time or allow the temperature to exceed 35°C (95°F). Mix suitably small quantities to ensure thorough mixing of the par A (silicone base) and part B (curing agent).
It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mix to completely expand and then collapse. After a further 1-2 minutes under vacuum, the mix should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture, so a suitably large container should be chosen.
Caution: prolonged vacuum will remove volatile components from the mix and may result in poor thick section cure and non-typical properties.
Note: If no vacuum de-airing equipment is available, air entrapment can be minimized by mixing a small quantity of par A (silicone base) and part B (curing agent), then using a brush, painting the original with a 1-2mm layer. Leave at room temperature until the surface is bubble free and the layer has begun to cure. Mix a further quantity of base and curing agent and proceed as follows to produce a final mold.

3. Pouring the Mixture and Curing
Pour the mixed Par A (silicone base) and Part B (curing agent) as soon as possible onto the original, avoiding air entrapment. The catalyzed material will cure to a flexible rubber within 24 hours at room temperature (22°C-24°C/ 71.6°F - 75.2°F) and the mold can then be separated from the original. If the working temperature is significantly lower, the cure time will be longer. If the room temperature or humidity is very high, the working time of the catalyzed mixture will be reduced. The final mechanical properties of the mold will be reached within 7 days.